Plaster - Plaster (English spelling)

Plastering materials for walls are broadly divided into gypsum plaster and dolomite plaster. There is also lime plaster, which is called plaster. Gypsum plaster is the most typical type of plaster, and is often simply called plaster.

Gypsum itself, like lime, is one of the oldest building materials. It was used in 2000 BC to seal the stone joints of the Egyptian pyramids and to decorate coffins, and was already used as a plaster at that time. Europe produces a large amount of high-quality natural gypsum, so it is highly regarded as a building material, and its fire-prevention value, especially in large urban fires, has made it a common building material. Plaster of Paris means burnt gypsum, and its origin is from gypsum plaster made in Paris. It was imported and used in Japan after the Meiji period, but it did not become the main building material. After the war, domestic production began due to its use in facilities of the occupying forces, and about 400,000 tons were produced annually, but production has since decreased, dropping to 186,000 tons in 1985 (Showa 60) and further to 30,000 tons in 2004 (Heisei 16).

Gypsum plaster can be further divided into several types depending on the raw materials used. The most common gypsum plaster is made mainly from calcined gypsum CaSO ₄・1/2H _​​2 O, but there are also plasters made solely or in combination with anhydrite CaSO ₄ (anhydrous gypsum) and anhydrite α-CaSO ₄・1/2H _​​2 O. There is no good quality natural gypsum in Japan, which is the raw material for gypsum plaster, and it is mainly by-product gypsum from the chemical industry, flue gas desulfurization gypsum, imported natural gypsum, etc. Calcined gypsum is made by baking the raw gypsum CaSO ₄・2H ₂ O (gypsum dihydrate) at 160-200°C. Anhydrite is produced when baked at 500-900°C. Meanwhile, anhydrite is produced in hot water at 100°C or higher. Currently, there are two types of gypsum plasters stipulated in the Japanese Industrial Standards (JIS): on-site mixed plasters, which are prepared by mixing aggregates and water at the construction site, and premixed plasters, which already contain aggregates and admixtures and can be used simply by adding water. Gypsum plasters are characterized by their resistance to shrinkage cracks, quick hardening, and beautiful finish.

Dolomite plaster is made by burning dolomite or dolomitic limestone to release the carbon dioxide gas contained in it, producing lightly burnt dolomite, which is then slaked (hydrated) with water. It has high plasticity and does not require the use of adhesives. Although the finished surface is inferior to that of gypsum plaster, it is easy to apply and inexpensive.

In addition, in the case of ceramic plaster, dental plaster, and even floor plaster that utilizes the self-leveling properties of gypsum, the word plaster is used to mean calcined gypsum or a gypsum composition.

[Norihiro Kudo]

Source: Shogakukan Encyclopedia Nipponica About Encyclopedia Nipponica Information | Legend

塗壁用材料で、石膏(せっこう)プラスターとドロマイトプラスターとに大別される。そのほかに石灰プラスターもあるが、これは漆食(しっくい)とよばれている。石膏プラスターはプラスターの代表的なもので、これを単にプラスターとよぶことも多い。

　石膏自体は石灰と同様にもっとも古い建築材料の一つで、紀元前2000年エジプトのピラミッドの石材の目地、棺の装飾に用いられていて、そのころからすでにプラスターとしての使い方がなされていた。ヨーロッパには良質の天然石膏が多量に産出するために、建材としての地位も高く、とくに都市における大火災に際して防火価値が認められ、建材としては一般化した材料である。Plaster of Parisは焼石膏を意味し、パリでつくられた石膏プラスターが語源となっている。日本においては明治以後に輸入され使用されたが、建材の中心にはならなかった。戦後占領軍の施設への使用により国内製造が始まり、年間約40万トンが生産されていたが、その後、生産量は減少し、1985年（昭和60）には18万6000トン、さらに2004年（平成16）には3万トンにまで減少している。

　石膏プラスターは、それに用いられる原料によって、さらに数種類に分けられる。もっとも一般的な石膏プラスターは焼石膏CaSO₄・1/2H₂Oを主原料とするが、硬石膏CaSO₄（無水石膏）、硬質石膏α-CaSO₄・1/2H₂Oを単味あるいは混合したプラスターもある。石膏プラスターの原料となる石膏は、国内に良質な天然品はなく、もっぱら化学工業からの副産石膏、排煙脱硫石膏、輸入天然石膏などである。焼石膏は、これら原料石膏CaSO₄・2H₂O（二水石膏）を160～200℃に焼いてつくる。また500～900℃で焼くと無水石膏となる。一方100℃以上の熱水中において硬質石膏ができる。現在、日本工業規格（JIS(ジス)）に規定されている石膏プラスターは、建築現場で骨材を調合し水と練り合わせて使用する現場調合プラスターと、あらかじめ骨材、混和材料等が混入されており、水を加えるだけで使用できる既調合プラスターの2種類である。石膏プラスターは収縮ひび割れが生じにくく、硬化が早く、仕上がりがきれいであるのが特徴である。

　ドロマイトプラスターは、ドロマイトやドロマイト質石灰石を焼成して含有する炭酸ガスを放出し、軽焼ドロマイトをつくり、これを水で消化（水和）したもので、可塑性が大きく、糊剤(のりざい)を使用する必要がない。仕上がり面は石膏プラスターに劣るが、塗りやすく割安である。

　なお、製陶用プラスターや歯科用プラスター、さらには、石膏のセルフレベリング性（自己水平性）を利用した床用プラスターなどの場合には、プラスターの語は焼石膏あるいは石膏組成物の意味で使われている。

［工藤矩弘］