Polyester - Polyester (English spelling)

Japanese: ポリエステル - ぽりえすてる（英語表記）polyester

A general term for polymers that have an ester bond -CO-O- in the main chain of the molecule. It is widely used in plastic bottles, plastic films, and synthetic fibers. There are thermoplastic saturated polyesters and thermosetting unsaturated polyesters. A typical example of saturated polyester is polyester fiber, while unsaturated polyester is a reinforced plastic with a glass fiber mat as the base material.

[Hiroshi Kakiuchi]

Manufacturing method

Terephthalic acid and ethylene glycol are mixed and heated. The resulting water is removed under reduced pressure and polycondensation takes place to produce polyethylene terephthalate (abbreviated as PET). Since polyethylene terephthalate has a melting point of 250-260°C, it can be melted in a nitrogen stream and extruded through a small hole to produce a single fiber. In Japan, this fiber is called "Tetoron." PET film is made from PET in a thin film form instead of thread, and is strong and does not tear easily. It is used as the base film for magnetic recording media, especially as PET film for magnetic tapes. PET bottles are also produced in large quantities, with production volume reaching 662,000 tons in 2001.

Polyester films with better strength have been developed, such as Teijin Q film, which replaces terephthalic acid with naphthalene-2,6-dicarboxylic acid, and polybutylene terephthalate (abbreviated PBT), which uses butanediol instead of ethylene glycol. In addition, glyptal resin (a type of alkyd resin), a thermosetting material made from phthalic acid and glycerin, may be added to polyester. Polyester synthetic fibers, along with polyamide (nylon) and polyacrylonitrile (acrylic fiber), are the main synthetic fibers.

[Hiroshi Kakiuchi]

"Plastic Technology Encyclopedia 13: Polyester Resins" (1970), edited and published by the Industrial Research Institute ; "Engineering Plastics" by Toshiro Kataoka et al. (1987, Kyoritsu Shuppan) ; "Saturated Polyester Resin Handbook" by Kazuo Yuki (1989, Nikkan Kogyo Shimbun) ; "Product Studies of Naphtha Systems" by Haruo Moriya (1997, Moriyama Shoten) ; "Chemistry of Polymer Structural Materials" by Yoshio Imai and Kaoru Iwata (1998, Asakura Shoten), edited by the Chemical Society of Japan ; "Comprehensive Analysis of Polyester Resins" (2000), edited and published by CMC ; "Evolving Chemical Technology - The Challenge of Unique Technology" edited by the Society of Chemical Engineers SCE Net (2003, Industrial Research Institute)"

Source: Shogakukan Encyclopedia Nipponica About Encyclopedia Nipponica Information | Legend

Japanese:

エステル結合-CO-O-を分子の主鎖中にもつ重合体（ポリマー）の総称。プラスチックボトル、プラスチックフィルム、合成繊維に大きな用途がある。熱可塑性の飽和ポリエステルと、熱硬化性の不飽和ポリエステルとがある。飽和ポリエステルの代表的なものはポリエステル繊維であり、不飽和ポリエステルはガラス繊維マットを基材にした強化プラスチックである。

［垣内　弘］

製法

テレフタル酸とエチレングリコールとを混合して加熱する。生成する水を減圧で飛ばして重縮合させていくとポリエチレンテレフタレート（略称PET(ペット)）になる。ポリエチレンテレフタレートは融点250～260℃であるから、窒素気流中で溶融して小さな孔(あな)から押し出すと単繊維になる。この繊維を日本では「テトロン」Tetoronとよんでいる。糸にするかわりに薄いフィルムにしたものがPETフィルムで、強靭(きょうじん)で容易に破れない。磁気記録媒体用ベースフィルム、とくに磁気テープ用PETフィルムとして使用されている。またPET製の瓶（ペットボトル）も多く生産され、その生産量は2001年（平成13）で66万2000トンである。

　強度的により優れたポリエステルフィルムとして、テレフタル酸をナフタレン-2,6-ジカルボン酸に置き換えたポリエステルフィルム（テイジンQフィルム）、エチレングリコールのかわりにブタンジオールを用いたポリブチレンテレフタレート（略称PBT）などが開発されている。そのほかにフタル酸とグリセリンとからなる熱硬化性のグリプタル樹脂（アルキド樹脂の一種）をポリエステルに入れる場合がある。ポリエステル系合成繊維は、ポリアミド系（ナイロン）、ポリアクリロニトリル系（アクリル繊維）とともに、合成繊維の主力を占めている。

［垣内　弘］

『工業調査会編・刊『プラスチック技術全書13　ポリエステル樹脂』（1970）』▽『片岡俊郎ほか著『エンジニアリングプラスチック』（1987・共立出版）』▽『湯木和男著『飽和ポリエステル樹脂ハンドブック』（1989・日刊工業新聞社）』▽『守屋晴雄著『ナフサ体系の商品学』（1997・森山書店）』▽『日本化学会編、今井淑夫・岩田薫著『高分子構造材料の化学』（1998・朝倉書店）』▽『シーエムシー編・刊『ポリエステル樹脂総合分析』（2000）』▽『化学工学会SCE・Net編『進化する化学技術――オンリー・ワン技術への挑戦』（2003・工業調査会）』