Melamine resin

Japanese: メラミン樹脂 - めらみんじゅし（英語表記）melamine resin

It is a type of amino resin (a general term for resins obtained by condensation of compounds containing the amino group _-NH2 with aldehydes), and is a thermosetting resin made from melamine and formaldehyde.

[Hiroshi Kakiuchi]

Manufacturing method

Melamine has three amino groups, and therefore six functional groups that react with formaldehyde. Depending on the mixing ratio and reaction conditions, a mixture of polymethylol melamine containing many methylol groups HOCH ₂ - or (CH ₂ OCH ₂ )nOH- is formed. This is the initial reaction product. The general manufacturing method is to mix 1 mole of melamine with 3.3 moles of formaldehyde and react them at about 80°C in a weak alkaline environment using sodium carbonate or ammonia. The aqueous solution becomes syrup-like. This syrup is dissolved in water-alcohol and mixed with a filler such as pulp, then dried and crushed into fine particles. At the same time, coloring materials and release agents are added and the mixture is pressurized and heated to produce a molded product.

[Hiroshi Kakiuchi]

Features and Applications

The molded products are characterized by their excellent heat resistance, water resistance, acid and alkali resistance, and arc resistance compared to urea resin (urea resin), which is also a thermosetting resin made from urea and formaldehyde. They are mainly used in electrical appliances, wiring devices, and tableware. Decorative boards, a representative product of melamine resin, have a melamine resin layer on the surface and a phenolic resin layer on the bottom. Aluminum plates are used for vehicles. This is to eliminate cracks and breakage caused by the brittleness of the melamine resin itself. It also prevents wrinkles in cotton, rayon, and staple fiber fabrics, reduces shrinkage due to washing, and gives them a texture similar to wool. Di- or trimethylol melamine butyl ether is used for this. Methylol melamine butyl ether is used as a paint, giving it a robust coating. This ether is dissolved in thinner to make varnish (melamine resin varnish). The coating has high hardness, is light in color and has a good luster, and is widely used for arts and crafts, furniture, etc. Japan's annual production volume is 159,000 tons (2002).

[Hiroshi Kakiuchi]

"Urea Resin Industry and Melamine Resin Industry" by Fuyama Itsuo (1950, Seibundo Shinkosha)" ▽ "Lectures on Plastic Materials: Melamine Resin" by Abe Michio (1961, Nikkan Kogyo Shimbun)" ▽ "Lectures on Plastic Materials: Urea and Melamine Resin" by Miwa Ichiro (1978, Nikkan Kogyo Shimbun)" ▽ "Adhesives" by Motoyama Takuhiko and Nagata Koji (1988, Kogyo Chosakai)"

Source: Shogakukan Encyclopedia Nipponica About Encyclopedia Nipponica Information | Legend

Japanese:

アミノ樹脂（アミノ基-NH₂を含む化合物とアルデヒドとの縮合によって得られる樹脂の総称）の一種で、メラミンとホルムアルデヒドからつくられた熱硬化性樹脂である。

［垣内　弘］

製法

メラミンはアミノ基を3個、したがってホルムアルデヒドと反応する官能基を6個もっている。配合比と反応条件によって多くのメチロール基HOCH₂-または(CH₂OCH₂)nOH-の入ったポリメチロールメラミンの混合物になる。これが初期反応物である。一般的な製造法は、メラミン1モルとホルムアルデヒド3.3モルを混合し、炭酸ナトリウムまたはアンモニアを用いて弱アルカリ性で80℃ぐらいで反応させる。水溶液がシロップ状になる。このシロップを水‐アルコールに溶解しパルプなどの充填(じゅうてん)剤に混合したのち、乾燥し粉砕して微粒にする。同時に着色材料、離型剤を加えて、加圧・加熱して成形物をつくる。

［垣内　弘］

特徴と用途

成形品の特徴は、尿素とホルムアルデヒドを原料とし、同じく熱硬化性樹脂であるユリア樹脂（尿素樹脂）に比べて耐熱、耐水、耐酸・耐アルカリ性に優れ、また耐アーク性も優れている。主として電気器具、配線器具、食器に使われている。メラミン樹脂の代表的な製品である化粧板は、表面がメラミン樹脂層で、下側はフェノール樹脂層になっている。車両用はアルミニウム板を用いる。これらはメラミン樹脂そのもののもろさに原因するひび割れ破損をなくすためである。また木綿やレーヨン、スフ織物のしわを防止し、洗濯による収縮率を小さくして羊毛に近い風合(ふうあい)を与える。これにはジまたはトリメチロールメラミンのブチルエーテルが使われる。塗料としてはメチロールメラミンのブチルエーテルが使われ、堅牢(けんろう)な皮膜を与える。またこのエーテルをシンナーに溶かしたものはワニス（メラミン樹脂ワニスmelamine resin varnish）である。塗膜の硬さは高く、淡色で光沢がよく、美術工芸品や家具などに広く用いられる。日本の年間生産量は15.9万トン（2002）である。

［垣内　弘］

『布山五雄著『尿素樹脂工業・メラミン樹脂工業』（1950・誠文堂新光社）』▽『安倍通夫著『プラスチック材料講座　メラミン樹脂』（1961・日刊工業新聞社）』▽『三輪一郎著『プラスチック材料講座　ユリア・メラミン樹脂』（1978・日刊工業新聞社）』▽『本山卓彦・永田宏二著『接着剤』（1988・工業調査会）』