…In addition, from a macroscopic point of view, fracture can be classified into creep fracture, fatigue fracture, etc., but the microscopic mechanism of fracture is often that microcracks occur in the inhomogeneous parts of the material structure due to stress concentration, and these grow or coalesce, leading to final fracture. In this case, fracture that does not involve a decrease in load is called stable fracture (stable crack growth), and final fracture that involves a decrease in load is called unstable fracture (unstable crack growth). Ductile fracture Brittle fracture [Kishi Teruo]. …