…When conditions that destroy this scale are applied or when dissolving substances are present, abnormal oxidation occurs, which becomes a problem in high temperature corrosion. When metals deform under stress, the surface film is destroyed, but if the rate at which the corrosion reaction begins at the break exceeds the rate at which it can be repaired, it develops into localized corrosion. The combination of wet corrosion conditions and mechanical destruction of the film can cause severe localized damage such as corrosion fatigue, impact corrosion, and stress corrosion cracking. …