Plaster bandage

Japanese: ギプス包帯 - ぎぷすほうたい（英語表記）plaster bandage

This is a typical hardening bandage that is widely used to immobilize affected areas such as fractures, and is an indispensable bandage in everyday orthopedic surgery.

Plaster bandages take advantage of the property of plaster powder (powdered gypsum) that solidifies when water is added. Plaster powder is calcium sulfate with half a molecule of water of crystallization, and when water is added it becomes hydrated calcium sulfate with two molecules of water of crystallization, solidifying and hardening. When this is heated to 107-130°C it becomes calcium sulfate with half a molecule of water of crystallization again, and can be powdered. The following equation shows these reactions.

CaSO ₄・1/2H ₂ O＋3/2H ₂ OCaSO ₄・2H ₂ O
A cast bandage is made by sprinkling this cast powder evenly on a roll of coarsely glued gauze cut to the appropriate width. Cast bandages are usually available in two-piece (15 cm wide) or three-piece (10 cm wide) rolls. When actually using it, it is soaked in lukewarm water and left to soak completely, then removed from the water, being careful not to let the cast powder run out, lightly squeezed, and used quickly. The cast bandage soaked in hot water is wrapped around the body in the same way as a normal roll, and while wrapping it until it is the appropriate thickness, it is rubbed well so that the bandage adheres to the body. The cast bandage gradually hardens. Recently, some bandages can be used with water instead of hot water, and some bandages harden quickly, but this does not necessarily mean that they are easy to use. After hardening, it is dried thoroughly to become a hard bandage. When applying a plaster bandage, a cotton bandage is usually placed underneath it, which is called a "bedded plaster bandage." In contrast, in special cases, the plaster bandage may be placed directly on the skin without an underlay, which is called a "non-bedded plaster bandage."

[Takashi Nagai]

Applications

Plaster bandages can be wrapped in any shape, harden quickly, and have strong retention, making them an excellent hardening bandage, so they are used in a variety of immobilization situations, including immobilizing the limbs and torso. A plaster bandage used to immobilize the torso is called a plaster corset.

It is also used as a stiffening bandage, or as a plaster bed or splint. A plaster bed is like a turtle shell and is used when a patient needs to lie on their back due to spinal disease. A plaster splint is a splint made of plaster bandage used to temporarily immobilize a fractured limb, and is widely used because it can be made to fit the body better than other splints made of wire mesh or metal plate.

Furthermore, plaster casts are essential in the creation of corsets and orthopedic limb braces, and are used to make impressions to create body models.

[Takashi Nagai]

Source: Shogakukan Encyclopedia Nipponica About Encyclopedia Nipponica Information | Legend

Japanese:

骨折などで患部を固定するために広く用いられている代表的な硬化包帯で、整形外科では日常なくてはならない包帯である。

　ギプス包帯は、ギプス末（石膏末(せっこうまつ)）が、水を加えることによって固形化する性質を利用したものである。ギプス末は2分の1分子の結晶水をもった硫酸カルシウムで、水を加えると2分子の結晶水をもった含水硫酸カルシウムとなり、固形化して硬化する。このものは107～130℃に熱することで、また2分の1分子の結晶水をもった硫酸カルシウムとなり、粉末化する。次の式はこれらの反応を示す。

　CaSO₄・1/2H₂O＋3/2H₂OCaSO₄・2H₂O
　ギプス包帯は、このようなギプス末を、目の粗い糊(のり)付きガーゼを適当な幅にしたガーゼ包帯に均等にまぶして巻軸帯(かんじくたい)としたものである。ギプス巻軸帯には普通2裂（15センチメートル幅）と3裂（10センチメートル幅）がある。実際に使用するときは、微温湯の中に浸して水分が完全に浸潤するのを待ち、ついでギプス末が流れ出ないように注意しながら湯の中から取り出し、軽く絞って速やかに用いる。その用法は、この湯に浸したギプス包帯を、普通の巻軸帯を巻くようにして身体に巻き付けるわけであるが、適当な厚さになるまで巻いていきながら、よくさすって包帯と包帯が密着するようにする。ギプス包帯はだんだんと硬化してくる。最近は湯でなく水でもよいもの、また硬化の速いものもあるが、それがかならずしも使いよいとは限らない。硬化後、十分に乾燥させれば硬い包帯となる。なお、ギプス包帯を巻くときは、普通その下敷きとして綿包帯などを巻くが、これを有褥(ゆうじょく)ギプス包帯という。これに対して特別の場合、下敷きなしでギプス包帯を直接皮膚の上に巻くことがあり、これを無褥ギプス包帯という。

［永井　隆］

用途

ギプス包帯はどのような形にも巻くことができ、硬化が速くて固定力も強く、優れた硬化包帯であるので、四肢や体幹の固定などあらゆる場合の固定に用いられる。体幹固定のギプス包帯は、ギプスコルセットとよばれる。

　また硬化包帯として身体に巻くほか、ギプスベッドやギプス副子(ふくし)として用いられる。ギプスベッドは、脊椎(せきつい)骨の疾患で仰臥(ぎょうが)安静（あおむけに寝たままでいる）が必要な場合に用いられるカメの甲らのようなものである。ギプス副子は、四肢の骨折などを一時的に固定するために用いられるギプス包帯でつくった副子で、ほかの金網製や金属板製などの副子に比べて身体によく適合するようにつくれるので、広く用いられる。

　さらにギプス包帯は、コルセットや四肢の整形外科的装具の作製になくてはならないものであり、身体のモデルをつくるための採型(さいけい)（型どり）に用いられている。

［永井　隆］

出典　小学館　日本大百科全書(ニッポニカ)日本大百科全書(ニッポニカ)について　情報 | 凡例

<<: Pseudo-asymmetric carbon atom

>>: Gibbs's paradox - Gibbs's paradox