Sulfite pulp - Aryusanparupu (English spelling) sulfite pulp

In the narrow sense, it is chemical pulp produced by the acid sulfite process using wood and other raw materials. Abbreviated as SP. The acid sulfite process uses a mixed aqueous solution of acid calcium sulfite and sulfurous acid as a cooking solution, processes the cellulose raw material at 140-150°C, and extracts pulp by dissolving non-cellulose substances such as lignin. Magnesium, sodium, or ammonium may be used instead of calcium in the cooking solution, but the term "sulfite process" simply refers to the calcium-based acid sulfite process. Pulp obtained by sufficient cooking (boiling to make pulp) is easily bleachable. It has a relatively high purity and medium strength. It was the mainstream of chemical pulp until around 1960 (Showa 35). Both unbleached and bleached pulp have excellent papermaking suitability, so they are the main raw material for most types of paper except heavy-duty wrapping paper. The most suitable raw material for sulfite pulp is softwood with a low resin content, but in Japan in the 1960s, resources became scarce and hardwood began to be used as a raw material. In the sulfite process, the cooking liquor is highly acidic, so even cellulose and hemicellulose are broken down and dissolved, reducing the strength and yield of the pulp. Hardwoods in particular are not suitable for papermaking pulp because they have short fiber length and a lot of hemicellulose. Taking advantage of their purity, they are used mainly as pulp for dissolving chemical raw materials such as rayon, carboxymethyl cellulose (CMC, chemical glue), and cellophane. However, overall demand has dropped significantly, and kraft pulp has taken over as the mainstream chemical pulp. Another major cause of the decline was the difficulty of treating the waste liquor.

In the broad sense, sulfite pulp includes pulp obtained by one or two-stage cooking of raw materials in acidic, neutral, or alkaline aqueous solutions of sulfite salts. The neutral or alkaline sulfite process is suitable for pulping non-wood materials such as hemp. The resulting non-wood sulfite pulp is used as a raw material for special high-quality paper such as machine-made Japanese paper.

Pulp obtained by mechanically defibrating hardwood and other materials after cooking them in a neutral solution of sulfite is specifically called neutral sulfite semi-chemical pulp. This has a high hemicellulose and lignin content and was used in extremely large quantities as it was suitable for hard paper, especially the medium base paper for cardboard. However, in the 1970s, the recovery of waste paper increased to reduce waste, and recycled pulp had to be used to manufacture paperboard, causing a sudden drop in both demand and production of neutral sulfite semi-chemical pulp.

[Akio Mita April 18, 2016]

Source: Shogakukan Encyclopedia Nipponica About Encyclopedia Nipponica Information | Legend

狭義では木材などを原料として酸性亜硫酸法で製造した化学パルプ。略称SP。酸性亜硫酸法は酸性亜硫酸カルシウムおよび亜硫酸の混合水溶液を蒸解薬液とし、セルロース原料を140～150℃で処理し、リグニンなどの非セルロース物質を溶出させてパルプを取り出す方法である。薬液中のカルシウムのかわりにマグネシウム、ナトリウム、アンモニウムを用いることもあるが、単に亜硫酸法といえばカルシウムベースの酸性亜硫酸法をさす。蒸解（煮てパルプ化すること）を十分に行って得られるパルプは易漂白性である。比較的純度が高く、中程度の強度を有する。1960年（昭和35）ごろまでは化学パルプの主流であった。未晒(みさらし)パルプも晒パルプも優れた抄紙(しょうし)適性をもつので、重包装紙以外のほとんどの種類の紙の主要原料となる。亜硫酸パルプの原料としては、樹脂分の少ない針葉樹材がもっとも適するが、日本では1960年代になって資源的に不足し、広葉樹材も原料とするようになった。亜硫酸法は蒸解薬液が強い酸性であるため、セルロースおよびヘミセルロースまで崩壊して溶出するので、パルプの強度と収率が低下する。とくに広葉樹材は繊維長が短くヘミセルロースが多いので、製紙用のパルプとしては適さない。もっぱらその純度を生かして人絹、カルボキシメチルセルロース（CMC、化学糊(のり)）やセロファンなどの化学原料の溶解用パルプとして使われている。しかし、全体として著しく需要が減り、化学パルプの主流としての位置はクラフトパルプに移った。また廃液の処理が容易でないことも衰退の大きな原因となった。

　広義の亜硫酸系パルプとしては、原料を亜硫酸塩の酸性、中性またはアルカリ性の水溶液で1段または2段蒸解して得られるパルプも入る。中性またはアルカリ性亜硫酸法は麻などの非木材のパルプ化に適する。得られた非木材の亜硫酸パルプは機械抄(す)き和紙など特殊高級紙の原料に用いられる。

　なお広葉樹材などを亜硫酸塩の中性溶液で蒸解後、機械的に解繊して得られるパルプは、とくに中性亜硫酸セミケミカルパルプとよばれる。これはヘミセルロースとリグニンの含有量が大きく、堅い紙、とくに段ボールの中芯(なかしん)原紙用に適するとして、きわめて大量に使われた。しかし1970年代になるとごみ減らしのため古紙回収が進み、再生パルプを板紙の製造に使わざるをえなくなり、中性亜硫酸セミケミカルパルプの需要と生産量は一挙に激減した。

［御田昭雄　2016年4月18日］

出典　小学館　日本大百科全書(ニッポニカ)日本大百科全書(ニッポニカ)について　情報 | 凡例